Effect of Al and Ti on High-Temperature Oxidation Behavior of CoCrFeNi-Based High-Entropy Alloys

Erdogan A., Döleker K. M., Zeytin S.

JOM, cilt.71, sa.10, ss.3499-3510, 2019 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 71 Sayı: 10
  • Basım Tarihi: 2019
  • Doi Numarası: 10.1007/s11837-019-03679-2
  • Dergi Adı: JOM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.3499-3510
  • Ondokuz Mayıs Üniversitesi Adresli: Hayır

Özet

CoCrFeNiAlxTiy high-entropy alloys were produced by the induction melting method and their oxidation behavior investigated when exposed to 1000°C for different durations. One or more body-centered cubic phases were found in all alloys, except CoCrFeNiTi0.5. In the CoCrFeNiTi0.5 alloy, two different face-centered cubic phases and one tetragonal sigma phase were detected. Scanning electron microscopy elemental analysis showed that all the alloys exhibited homogeneous microstructure. Energy-dispersive x-ray spectroscopy analysis revealed that Cr and Fe elements were enriched in one phase and Al-Ni-Ti elements in another. The presence of Ti negatively affected the oxidation behavior. According to the oxidation test results, dominant Al2O3 formation was observed in the CoCrFeNiAl0.5 and CoCrFeNiAlTi0.5 alloys. As a result, these two alloys exhibited the best performance among the five high-entropy alloys in terms of mass gain and oxide thickness.