Fabrication and mechanical characterization of rare earth permanent magnet SmCo5 films

Kuru M., Sahin O., Ozarslan S., Ozmetin A. E.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.694, ss.726-732, 2017 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 694
  • Basım Tarihi: 2017
  • Doi Numarası: 10.1016/j.jallcom.2016.10.089
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.726-732
  • Anahtar Kelimeler: SmCo5 thin film, Mechanical properties, Nanoindentation, THIN-FILMS, NANOMECHANICAL PROPERTIES, NANOINDENTATION, HARDNESS
  • Ondokuz Mayıs Üniversitesi Adresli: Evet

Özet

This study reports mechanical properties of rare earth permanent magnet (REPM) SmCo5 thin films fabricated by RF magnetron sputtering technique. 1 mu m thick SmCo5 thin films were grown on Si (100) substrate at room temperature, and later they were annealed at 400 degrees C. Great care has been taken to decrease O-2 in the chamber throughout deposition. Mechanical and Structural properties of SmCo5 thin films were researched using the nanoindentation and in situ scanning probe microscopy (SPM), Grazing Incident X-ray Diffraction (GIXRD) and Scanning Electron Microscopy (SEM) techniques. Nanoindentation-induced plasticity of SmCo5 thin film was characterized by in situ SPM imaging of indented cross-sections. Nanoindentation results show load-displacement curves are continuous and smooth that there is no pile-up and sink-in behavior. Furthermore, both elastic modulus and nano hardness values of REPM SmCo5 exhibit peak load dependence. Nanohardness increases with increasing indentation test load, while the reduced modulus decrease with increasing indentation test load. The obtained values of the intrinsic nanohardness and intrinsic reduced modulus are 3.47 +/- 0.07 GPa and 43.09 +/- 1.60 GPa, respectively. (C) 2016 Elsevier B.V. All rights reserved.